Quartz Stone, Marble, Unsaturated Polyester Concrete Resin with Lighter Color, Low Shrinkage, Air Drying

• Customization: Available
• Color: Transparent Liquid+Yellow
• Appearance: Light Yellow Transparent Liquid
• Gel Time Test: Resin 50g
• Features: Light Color, Low Shrinkage, Air-Drying
• Usage: Medium Temperature Production
• Transport Package: Wooden Box
• Trademark: Rule
• Origin: Changzhou China
• HS Code: 3907913000
• Package Size: 57.10cm * 57.10cm * 89.00cm
• Package Gross Weight: 220.000kg

Product Description

Artificial marble, polyester concrete resin
Artificial marble resin is widely used in the production of products such as kitchen countertops, toilet wash-face dressing tables and bathtubs. It has a complete variety and has its own characteristics. Polyester concrete resin is suitable for the production of cellar covers, fire hydrants and other products. The products have high compressive strength and service life. long feature
Quartz Stone, Marble, Polyester Concrete Resin
UPR for cultured marble is used for the casting of cultured marble, tabletop, bath tub, etc. UPR for Polymer concrete is used for products manhole covers and hydrant.

Product Description

A: RC NX-37 Unsaturated Polyester Resin
 

1.Features and usage:

RC NX-37 is used to produce translucent, good three-dimensional artificial marble/agate products.It has light color, low shrinkage, air-drying, weather resistance, and good hot water resistance. It is suitable for medium temperature production to make high-end bathroom facilities.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	Light yellow transparent liquid	B80101
Hazen	---	≤50	B42300
Viscosity	Pa•s	0.50~0.60	B54953
Gel time	min	3.7~4.7	C82012
Proportion	---	1.065~1.085	JIS K 6901.4.1.2

Note: Gel time test: resin 50g; accelerator RP-153 1.0%; curing agent Butanox M-50 1.0%
 

3.Physical properties of casting body (for reference only)

Item	Unit	Index	Testing method
Tensile Strength	MPa	75.4	GB/T2567-2008
Elastic Tensile Modulus	MPa	3090
Elongation at Break	---	4.02%
Bending Strength	MPa	118.0	GB/T2567-2008
Modulus of elasticity ( MOE)	MPa	3310
Impact Strength	KJ/m2	18.0	GB/T2567-2008
Heat Deflection Temperature	ºC	109	GB/T1634-2004
Bacol hardness	---	42	GB/T3854-2005
Relative Density	---	1.16	GB/T1463-2005

Note:

1.the sample method of casting system:GB / t8237-2005, curing system: accelerator rp-153: 1.0%; Curing agent butanox m-50:1%

2.Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 120 ºC × Two hours.

 

4.Instructions:

RC nx-37 resin 100 units
Medium temperature curing agent 0.3 ~ 0.7
Al(OH)3 200 units
 

5.Notices:

The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.

 

 

Product Parameters

B: RC TP-156 Unsaturated Polyester Resin
 

1.Features and usage:

RC TP-156 is used to produce translucent, three-dimensional artificial marble/agate products (eg: washing and dressing table, kitchen countertop, bathtub). It is a kind of pre-accelerated resin with air-drying character, can be colored vividly with a small amount of pigment; excellent curability, short molding cycle, light cured material, high heat distortion temperature, small product warpage, UV stability and good stain resistance.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	Light violet liquid	B80101
Viscosity	Pa•s	1.30~1.70	B54953
Gel time	min	10.0~16.0	C82801

Note: Gel time test: resin 50g; curing agent Butanox M-50 1.0%
 

3.Physical properties of casting body (for reference only)

Item	Unit	Factual Value		Testing Method
		Casting body	Marble
Tensile Strength	MPa	66	33.1	GB/T2567-2008
Elastic Tensile Modulus	MPa	4060	12300
Elongation at Break	---	1.7%	0.30%
Bending Strength	MPa	108	49.3	GB/T2567-2008
Modulus of elasticity ( MOE)	MPa	3900	10600
Impact Strength	KJ/m2	7	2.55	GB/T2567-2008
Heat Deflection Temperature	ºC	90	130	GB/T1634-2004
Bacol hardness	---	47	62	GB/T3854-2005
Water-absorbing(25ºC,24h)	---	0.3%	0.029%	GB/T1462-2005

Note:
1) The casting system sample method: GB/T8237-2005, and the curing system: Huangyan MEKP 1.0%;
2) Post-curing treatment of casting body: room temperature×24 hours+60ºC×3 hours+110ºC×2 hours;
3) Marble post-curing treatment: room temperature × 24 hours + 60° C. × 1 hour + 80° C. × 2 hours + 130° C. × 2 hours.
 

4.Instructions:

RC TP-156 resin 100 units
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 200 units
 

5.Notices:

The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.


C: RC TP-254 Unsaturated Polyester Resin
 

1.Features and usage:

RC TP-254 is an isophthalic acid type unsaturated polyester resin, used to produce rigid, heat-resistant artificial marble (bathtubs, wash basins). Combined with a low shrinkage agent, it has excellent low shrinkage and can be quickly formed at high temperature.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	Light yellow transparent liquid	JIS K 6919.5.1.3
Gardner	---	≤3	JIS K 6901.5.2
Viscosity	Pa•s	0.42~0.52	JIS K 6901.5.5.1
Gel time	min	4.2~7.8	JIS K 6901.5.10

Note: Gel time test: resin 50g; accelerator RC 2.0%; curing agent Butanox M-50 2.0%
 

3.Physical properties of casting body and marble (for reference only):

Item	Unit	Factual Value		Testing Method
		Casting body	Marble
Tensile Strength	MPa	62.8	28.2	GB/T2567-2008
Elastic Tensile Modulus	MPa	3500	10200
Elongation at Break	---	2.15%	0.31%
Bending Strength	MPa	102	53.9	GB/T2567-2008
Modulus of elasticity ( MOE)	MPa	3240	9310
Impact Strength	KJ/m2	11.4	2.98	GB/T2567-2008
Heat Deflection Temperature	ºC	128	>140	GB/T1634-2004
Bacol hardness	---	42	60	GB/T3854-2005
Hydroscopic Rate(25ºC,24h)		0.209%	---	GB/T1462-2005

Note:

1.the casting system and sample method: GB / t8237-2005, and the curing system is rp-153 1.0%; The MEKP of Huangyan is 1.0%;

2. Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 120 ºC × 2 hours;
3).Post curing treatment of marble: room temperature × 24 hours + 60 ºC × 1 hour + 80 ºC × 2 hours + 130 ºC × Two hours.
 

4.Instructions:

RC TP-254 Resin 100 units
Accelerator RC-153 1.0
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 200 units
 

5.Notices:

1.When the construction environment temperature is high and the gel time is short, the amount of curing agent cannot be reduced, and the gel retarder RC-406 should be added as needed.
2.The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.


D: RC-H-1036L Unsaturated Polyester Resin
 

1.Features and usage:

RC-H-1036L unsaturated polyester resin is used to produce artificial marble countertops and sanitary ware. It has good water resistance, crack resistance and pollution resistance. Used in conjunction with colorless accelerator RP-153, the cured product has a light color and low exothermic peak.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	Light yellow transparent liquid	B80101
Hazen	---	≤80	B42300
Viscosity	Pa•s	0.60~0.80	B54953
Gel time	min	10.0~18.0(from May to October)	HR-1040
		6.0~10.0(November to next April)
Non-volatile material	%	64.0~68.0	B22301

Note: Gel time test: resin 50g; accelerator RCA: 1.5%; curing agent Butanox M-50: 1.0%.
 

3.Physical properties of casting body and marble (for reference only):

 

Item	Unit	Factual Value		Testing Method
		Casting body	Marble
Tensile Strength	MPa	69.2	22.4	GB/T2567-2008
Elastic Tensile Modulus	MPa	3760	11300
Elongation at Break	---	2.48%	0.22%
Bending Strength	MPa	129	55.0	GB/T2567-2008
Modulus of elasticity ( MOE)	MPa	3890	11300
Impact Strength	KJ/m2	11.7	3.23	GB/T2567-2008
Heat Deflection Temperature	ºC	65	90	GB/T1634-2004
Bacol hardness	---	43	66	GB/T3854-2005

Note:
1.The sample preparation method of casting system:GB / t8237-2005, and the curing system is rp-153 1%; Curing agent butanox m-50 1%; 2) Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 80 ºC × 2 hours;

2.Post curing treatment of marble: room temperature × 24 hours + 60 ºC × 1 hour + 80 ºC × 2 hours + 100 ºC × Two hours.

 

4.Instructions:

RC-H-1036L Resin 100 units
Accelerator RC-153 1.0
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 200 units
 

5.Notices:

1.When the construction environment temperature is high and the gel time is short, the amount of curing agent cannot be reduced, and the gel retarder RC-406 should be added as needed.
2.The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.


E: RC TPH-3143 Unsaturated Polyester Resin
 

1.Features and usage:

RC TPH-3143 is a kind of pre-accelerated unsaturated polyester resin in bisphenol A type with high refractive index resin,low exothermic;also good corrosion resistance, used in conjunction with aluminum hydroxide, used to produce highly transparent, three-dimensional artificial marble/agate products (Example: Washing and dressing table, kitchen countertop); The product has small warpage and deformation.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	Light violet green liquid	B80101
Viscosity	Pa•s	1.00~1.30	B54953
Gel time	min	25.0~35.0	JIS K 6901.5.10

Note: Gel time test: resin 50g; curing agent Butanox M-50 1.0%
 

3.Casting performance (for reference only)

Item	Unit	Index	Testing method
Tensile Strength	MPa	64.3	GB/T2567-2008
Elastic Tensile Modulus	MPa	3830
Elongation at Break	---	2.26%
Bending Strength	MPa	105	GB/T2567-2008
Modulus of elasticity ( MOE)	MPa	3940
Impact Strength	KJ/m2	10.6	GB/T2567-2008
Heat Deflection Temperature	ºC	67.8	GB/T1634-2004
Bacol hardness	---	40	GB/T3854-2005

Note:
1) The sample preparation method of casting:GB / t8237-2005, and the curing system is M50 1.0%;
2) Post curing treatment: room temperature × 24 hours + 60 ºC × 3 hours + 80 ºC × 2 hours;
3) marble post curing treatment: room temperature × 24 hours + 60 ºC × 1 hour + 80 ºC × 2 hours + 90 ºC × Two hours.
 

4.Instructions:

RC TPH-3143 resin 100 units
Curing agent (methyl ethyl ketone peroxide MEKPO) 1.0 or more
Al(OH)3 100 units
 

5.Notices:

1.When the construction environment temperature is high and the gel time is short, the amount of curing agent cannot be reduced, and the gel retarder RC-406 should be added as needed.
2.The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.

Recommended Products

Company Profile

Founded in 2002, Changzhou Rule Composite Material Co., Ltd, is a enterprise engaged in in manufacturing high-performance unsaturated polyester resin, gel coat, glass fiber reinforced composite materials and other related products, also professional in research, development as well as technical consulting and services of composite materials.

Rule Composite Material covers an area of 50, 000 square meters, with a modern office building, an independent R& D center and a high-standard production workshop, equipped with the leading DCS automatic control production device. We also have a strong and advanced quality control department and technical support laboratory.

RULE focuses on the production of excellent-quality and creative-design resin products, so it is trustworthy. Our sweat and wisdom witness the footprints of yesterday's struggle, passion and dream fulfill today's victory. Forging ahead to make innovation in market economy, pursuing value of "innovation, creativity, sharing" in practice, it harvests a stream of praises and honors.

 

 

Certifications

Packaging & Shipping

FAQ

1. How can I get a sample?
    Small quality of sample in stock will be free, but the freight will be charged.

2. Are you able to adjust the formula to meet our requirement?
    We have our own technical department, after you test the sample, please tell us your detailed requests, we are able to adjust the resin according to your requests, and bring better properties to your finished products.

3. What is the lead time for mass production?
    Honestly, it depends on the quantity. We will try our best to make the production plan according to your ETA.

4. What is your terms of payment?
    100% full payment for the 1st trial order; from next order, 30% payment in advance, 70% payment after buyer get the B/L copy. We also accept L/C if you need.