Solar Resin for Lighting Tiles for Continuous Panel and Hand Lay-up Applications From China Factory Has Good Weather Resistance and Good Glass Fiber Wettability

• Customization: Available
• CAS No.: Polyester Resin
• Formula: Polyester Resin
• Model NO.: UPR-005
• EINECS: Polyester Resin
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Light Yellow Transparent Liquid
• Polyester Resin MOQ: 1000kgs
• Transport Package: Wooden Box
• Specification: Can be customized
• Trademark: Rule
• Origin: Changzhou China
• HS Code: 3907910000
• Production Capacity: 50000kg
• Package Size: 57.10cm * 57.10cm * 89.00cm
• Package Gross Weight: 220.000kg

Product Description

Lighting tile resin
The resin used for lighting tile has good wettability to glass fiber and is suitable for hand lay-up or continuous molding by machine. The lighting panel made with alkali-free cloth has high light transmittance and good weather resistance.
 Daylight Resin
UPR for translucent panel can rapidly wet reinforcement.These series are suitable for continuous panel and  hand lay-up application. The FRP panels provide high translucent and good weather resistance.

Product Description

A:RC-C-1060 Unsaturated polyester resin
1.Features and usage:

RC-C-1060 is a kind of highly activity, flame-retardant, light-colored unsaturated polyester resin. It has low viscosity and good wettability to glass fiber, suitable for hand lay-up, RTM and machine-made molding processes. RC-C-1060 is used for making flame-retardant products such as translucent lighting covers, corrugated tiles, solar water heater parts, etc. Products made of it has high light transmittance, good flame retardancy, good weather resistance, also high mechanical strength.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	light yellow transparent liquid	GB/T8237.6.1.1-2005
Hazen	---	≤60	B 42300
Viscosity	Pa·s	0.15~0.25	GB/T 7193.4.1-2008
Gel time	min.	16.0~26.0	GB/T 7193.4.6-2008
Non-volatile material	---	(64.0~70.0)%	B 22301

Note: Gel time measurement: RCA 2.0%, curing agent Butanox M50 2.0%.
 

3.Instructions:

RC-C-1060 100 units
Curing agent Butanox M-50 2 units
Colorless accelerator 0.5~2 units (the amount depends on the temperature)
 

4.Physical properties of casting body (for reference only)

Item	Unit	Factual Value	Testing Method
Tensile Strength	MPa	50	GB/T2567-2008
Elongation at Break	---	3.0%	GB/T2567-2008
Bending Strength	MPa	95	GB/T2567-2008
Heat Distortion Temperature	ºC	64	GB/T1634-2004
Oxygen Index	---	28%	GB/T2408-2008

Note:
1) The manufacturing method of the pouring body: according to GB/T8237-2005, the thickness of the oxygen index test piece is 3mm; the curing system: curing agent MEKP (Huangyan) 2.0%, colorless accelerator E5 1.0%;
2) Post-treatment of the pouring body: room temperature × 24 hours + 60°C × 3 hours + 80°C × 1 hour.
 

5.Notices:

The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.

 

 

Product Parameters

B:RC-C-1071(Pre-accelerated resin)Unsaturated polyester resin
 

1.Features and usage:

RC-C-1071 (pre-accelerated) is a pre-accelerated ortho-phthalic unsaturated polyester resin with high light transmittance.The glass fiber made with it have good weather resistance. It has low viscosity and is well permeant to glass fiber. Used with the alkali-free cloth, it is suitable for the production of continuous forming transparent board by mechanism
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	Lilac transparent liquid	GB/T 8237.6.1.1-2005
Viscosity	Pa·s	0.15~0.25	GB/T 7193.4.1-2008
Gel time	min.	18.0~26.0	GB/T 7193.4.6-2008
Non-volatile material	%	55.0~61.0	GB/T 7193.4.3-2008

Note: gel time determination: curing agent MEKPO (Huangyan):2.0%.
 

3.Physical properties of casting body (for reference only)

Item	Unit	Factual Value	Testing Method
Tensile Strength	MPa	50	GB/T 2567-2008
Elongation at Break	%	1.5	GB/T 2567-2008
Bending Strength	MPa	115	GB/T 2567-2008
Heat Distortion Temperature	ºC	73	GB/T 1634-2004
Bacol Hardness	---	46	GB/T 3854-2005

Note:

1.the casting method:GB / t8237-2005,curing system:MEKPO (Huangyan) 2.0%;

2) Post treatment of casting body: room temperature × 24 hours + 60 ºC × 3 hours + 80 ºC × One hour.
 

4.Instructions

RC-C-1071 (pre-promotion) 100 units
Initiator (Methyl ethyl ketone peroxide MEKPO) 2 units
 

5.Notices:

The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.


C: RC-C-1092JX Unsaturated polyester resin

1.Features and usage:

RC-C-1092JX is a general-purpose o-phthalic flame-retardant unsaturated polyester resin. FRP products made of it have high light transmittance and good weather resistance. It has low viscosity and is well permeant to glass fiber, suitable for the production of machine-made continuous forming transparent board when matched with alkali-free cloth.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	Light green transparent liquid	GB/T 8237.6.1.1-2005
Viscosity	Pa·s	0.15~0.25	GB/T 7193.4.1-2008
Gel time	min	17.5~32.5	JIS K 6901.5.10
Non-volatile material	%	62.8~68.8	B 22301

Note: gel time determination: accelerator RCA: 2%; Curing agent butanox m-50: 2.0%.
 

3.Physical properties of casting body (for reference only

Item	Unit	Factual Value	Testing Method
Tensile Strength	MPa	35.3	GB/T 2567-2008
Elongation at Break	---	9.25%	GB/T 2567-2008
Bending Strength	MPa	56.4	GB/T 2567-2008
Heat Distortion Temperature	ºC	50.0	GB/T 1634-2004
Bacol Hardness	---	20	GB/T 3854-2005
Oxygen Index	%	25	GB/T 2406-2008

Note:

1.the casting method:GB / t8237-2005, and the curing system is RCA 2.0%; Curing agent butanox m-50 2.0%.

2) Post treatment of casting body: room temperature × 24 hours + 60 ºC × 3 hours + 80 ºC × One hour.

4. Instructions
RC-C-1092JX 100 units
Initiator (Methyl ethyl ketone peroxide MEKPO) 2 units
Accelerator RCA 0.5~2 units (the amount depends on the temperature)

5.  Notices:
The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 
6.  Product Safety Data (SDS):
Before using this product, please read the SDS of this product in detail.


D: RC-191 General Type Unsaturated Polyester Resin
 

1.Features and usage:

Product made of The RC-191 unsaturated polyester resin has good mechanical strength, low viscosity, good UV resistance and is well permeant to glass fiber. It is especially suitable for hand lay-up process to make translucent FRP tiles.
 

2.Technical index of liquid resin (25 ºC):

Item	Unit	Index	Testing method
Appearance	---	light yellow transparent liquid	GB/T8237.6.1.1
Viscosity	Pa·s	0.26~0.43	GB/T7193.4.1
Gel time	min	9.1~16.9	GB/T7193.4.6
Acid value	mgKOH/g	28.0~36.0	JIS K 6901 5.3
Non-volatile material	---	(61.0~67.0)%	GB/T7193.4.3

Note: gel time determination: resin 100g, "E" liquid 4ml " 0 g of "H" paste.
 

3.Physical properties of casting body (for reference only

Item	Unit	Factual Value		Testing Method
		Casting Body	FRP
Tensile Strength	MPa	56	---	GB/T2568-1995
		---	280	GB/T1447-2005
Bending Strength	MPa	108	---	GB/T2570-1995
		---	344	GB/T1449-2005
Heat Distortion Temperature	ºC	65	---	GB/T1634-2004
Bacol Hardness	---	49	60	GB/T3854-2005

Note:
1) The sample preparation method of casting body and FRP is implemented according to GB/T8237-2005, curing system: accelerator RCA 1.0%, curing agent Butanox M-50 2.0%;
2) Post-curing treatment of casting body: room temperature × 24 hours + 60°C × 3 hours + 75°C × 1 hour;
3) FRP 4mm thick, post-curing treatment: room temperature × 24 hours + 80°C × 8 hours.
 

4.Instructions

Rc-191 100 units
Initiator  ( Methyl ethyl ketone peroxide (MEKPO) 2 phr
accelerator   RCA 0.5~2   Portion (amount depends on temperature)
 

5.Notices:

The product should be stored in a cool place below 25ºC, avoid fire, and keep away from heat and radiation sources. The shelf life of storage below 25ºC is 3 months after leaving the factory.
 

6.Product Safety Data (SDS):

Before using this product, please read the SDS of this product in detail.

Recommended Products

 

Company Profile

Founded in 2002, Changzhou Rule Composite Material Co., Ltd, is a enterprise engaged in in manufacturing high-performance unsaturated polyester resin, gel coat, glass fiber reinforced composite materials and other related products, also professional in research, development as well as technical consulting and services of composite materials.
Rule Composite Material covers an area of 50, 000 square meters, with a modern office building, an independent R& D center and a high-standard production workshop, equipped with the leading DCS automatic control production device. We also have a strong and advanced quality control department and technical support laboratory.
RULE focuses on the production of excellent-quality and creative-design resin products, so it is trustworthy. Our sweat and wisdom witness the footprints of yesterday's struggle, passion and dream fulfill today's victory. Forging ahead to make innovation in market economy, pursuing value of "innovation, creativity, sharing" in practice, it harvests a stream of praises and honors.

Certifications

Packaging & Shipping

 

FAQ

1. How can I get a sample?

Small quality of sample in stock will be free, but the freight will be charged.

2. Are you able to adjust the formula to meet our requirement?
We have our own technical department, after you test the sample, please tell us your detailed requests, we are able to adjust the resin according to your requests, and bring better properties to your finished products.

3. What is the lead time for mass production?
Honestly, it depends on the quantity. We will try our best to make the production plan according to your ETA.

4. What is your terms of payment?
100% full payment for the 1st trial order; from next order, 30% payment in advance, 70% payment after buyer get the B/L copy. We also accept L/C if you need.